Ihe na -agba ọkụ maka ala ọkụ ọkụ eletrik ferroalloy
Ihe na -agba ọkụ maka ala ọkụ ọkụ eletrik ferroalloy
A na -eji ihe a maka owuwu na njikọta nke ala nke nchacha ọkụ nke ọkụ eletrik ferroalloy.
Usoro nrụpụta: A na -eji ihe ọkụkụ na -emegharị ala nke ọkụ eletriki ferroalloy nke ájá sịntetik nke ụlọ ọrụ anyị mepụtara wee jiri nha ururu dị mma wee were ya. Ihe a na -arụ ọrụ dị mma nke ukwuu, nnukwu njupụta dị elu, ike mkpakọ dị elu, nhịahụ dị mfe, nguzogide corrosion siri ike, wdg.
| Ihe ngosi na akara ule | DHL-83 | |
| mmiri mejupụtara （%） | MgO | > 84 |
| CaO | 7-9 | |
| Fe2O3 | 5-6 | |
| SiO2 | ||
| AI2O3 | ||
| IL | ||
| Njirimara nke anụ ahụ | Granularity mejupụtara (mm) | 0-6 |
| Okpokoro urughuru (g/cnP) | > 3.30 | |
| Ike mgbe sintering (1300 ° CX3h) (Mpa) | > 8-14 | |
| Ike mgbe sintering (1600 ° CX3h) (Mpa) | > 39 | |
| Ijikọta atụmatụ | kpara | |
| Ọnụego mgbanwe ahịrị (1300 ° CX3h) (%) | +0.1—+0.17 | |
| Ọnụego mgbanwe ahịrị (1600 ° CX3h) (%) | -1.8 –2 | |
| Oke okpomọkụ ọrụ (° C) | 1950 ° C | |