Sintering method of furnace wall lining of induction furnace

The furnace wall lining of the induction furnace slowly heats up the charge to melt, and keeps it at 1580°C (±20°C) for half an hour.

When the molten iron temperature is greater than 1500°C, the temperature is generally monitored every 10 minutes.

Feeding starts when the initial charge melting reaches about 30%.

Each feeding should be carried out before the last time the material is completely melted. Be careful not to produce shed material, and continue feeding until the furnace is full.

ld use relatively clean metal materials, and try to avoid materials with complex composition, rust and oil, especially oil-impregnated scrap iron. The material with low melting point and good fluidity will increase the penetration of the furnace wall.