Use of unshaped refractory ramming material for intermediate frequency coreless induction furnace

The baking and heating system of the unshaped refractory ramming material used in the intermediate frequency coreless induction furnace varies according to the different raw materials. The main purpose of the ramming material is to build the lining of the tempering furnace that is in direct contact with the melt, such as the blast furnace tapping channel, the bottom of the steelmaking furnace, the inner lining of the induction furnace, the top of the electric furnace, and the blanking part of the rotary kiln. In addition to the entire furnace lining, large-scale prefabricated components can also be manufactured. For ramming materials containing inorganic chemical binders, they can be demolded and baked after they harden to the proper strength. Materials containing thermoplastic carbon binders can be demolded after being cooled to have proper strength. After demolding It should be heated quickly to carbonize it before use. It does not contain binder materials that harden at room temperature, and is often sintered with a mold after tamping. For the sintering of the lining of the intermediate frequency coreless induction furnace with unshaped refractory ramming material, a suitable thermal system can be used for sintering.

The unshaped refractory ramming material used for the intermediate frequency coreless induction furnace is to maintain the furnace and the coil. Strong corrosion resistance, corrosion resistance and fineness.