Машина высокочастотного индукционного нагрева for bed rail quenching process

High-frequency induction heating machine for surface hardening process of workpiece

①Name of high-frequency induction heating surface hardening work piece CA6140 lathe bed rail high-frequency hardening inductor structure, the material used is HT300.

②High frequency induction heating surface quenching heat treatment technical conditions, medium frequency quenching electrical parameters: primary voltage, 520V; incoming line current, 150A; primary coil turns, 12 turns; secondary coil turns, 120kW; power factor, 90% .

③High-frequency induction heating surface quenching heat treatment process specification: a. The gap between the inductor and the guide rail surface is 1.5-2mm. b. Moving speed 4mm/min. Quenching temperature 900℃. d. Quenching medium water. e. Cooling method: continuous spraying.

④ Анализ процесса термообработки закалкой поверхности с помощью индукционного нагрева промежуточной частоты a. Твердость После высокочастотной закалки твердость достигает 45 ～ 55HRC. б. Глубина затвердевшего слоя 2 мм. c. Микроструктура. Упрочненный слой представляет собой скрытокристаллический мартенсит тонкой игольчатой ​​формы. Графит. Есть небольшое количество эвтектики фосфора без явного переходного слоя. d. Деформация изгиба, углубление посередине меньше или равно 0.5 мм.