Izitena eziphefumlayo kunye nezitena zokuhlala

Izitena eziphefumlayo kunye nezitena zokuhlala

Isitena esinokungena emoyeni se-ladle esenziwe yinkampani yethu senziwe nge-corundum eyenziwe ngeplate, i-spinel, i-chromium oxide kunye nezinye izinto, ezenziweyo, ezikhutshiweyo kwaye zahlanganiswa. Ibonakaliswe ngamandla aphezulu, ukumelana nokhukuliseko, ukumelana nokhukuliseko, kunye nokuqina komoya ophezulu. Zilungele zonke iintlobo zokusetyenziswa kweeleli. Ngokukodwa, izitena zomoya ezisandula kuphuhliswa eziqulethe izixhobo ze-nitride zinokumelana kakuhle nokubola, akukho lula ukungena kwisinyithi, kwaye zinezinga eliphezulu lokubetha. Zezona mveliso zithandwa ngezitena zomoya kubathengi.

Izalathi zomzimba kunye nezemichiza zezitena ezinokuphefumla

Inombolo yekhadi ZX-TQ11 ZX-TQ12 ZX-TQ13 ZX-TQ21
Al 2 O 3 %, ≥ 92     88
IAl 2 O 3 + MgO %, ≥   92    
Al 2 O 3 + Cr 2 O 3 %, ≥     92 Isi-5 (iSialon)
Unizi lolwapho kuyiwa khona g / cm 3, ≥ 3.10 3.10 3.12 3.10
Amandla amakhulu MPA, ≥ 90 90 90 90
Utshintsho lomgca (1500 ℃ × 3h),% ± 0.2 ± 0.2 ± 0.2 ± 0.2
Ukuqina komoya m 3 / h (0.3MPa) ≥ 10 10 10 10

 

Inkcazo yePhysical and Chemical ye-Breathable Block kunye ne-Nozzle Block

Inombolo yekhadi ZX-ZYS1 ZX-ZYS2 ZX-ZYS3 ZX-ZYS4
Al 2 O 3 %, ≥ 92     83
IAl 2 O 3 + MgO %, ≥   92    
Al 2 O 3 + Cr 2 O 3 %, ≥     92  
Unizi lolwapho kuyiwa khona g / cm 3, ≥ 3.10 3.10 3.12 2.85
Amandla amakhulu MPA, ≥ 90 90 90 80
Utshintsho lomgca (1500 ℃ × 3h),% ± 0.2 ± 0.2 ± 0.2 ± 0.2