Yintoni umahluko phakathi izitena alumina eliphezulu nezitena zodongwe

a. I-refractoriness ye-high-refractory alumina izitena iphezulu kunezitena zodongwe kunye nezitena ze-semi-silica, ezifikelela kwi-1750 ~ 1790 ℃, eyona nto i-high-grade refractory.

b. Umthwalo wokuthambisa ubushushu Ngenxa yokuba iimveliso ze-aluminiyam eziphezulu zine-Al2O3 ephezulu, ukungcola okuncinci, kunye neglasi encinci ye-fusible, iqondo lokushisa lomthwalo liphezulu kunolo lwezitena zodongwe, kodwa ngenxa yokuba iikristale ze-mullite azenzi isakhiwo sothungelwano, iqondo lokushisa lokuthambisa umthwalo lisekhona phezulu njengezitena zesilika.

c. Ukumelana ne-slag isitena esiphezulu se-alumina siqulethe i-Al2O3 eninzi, esondele kwizixhobo eziphikisayo ezingathathi hlangothi, kwaye inokumelana nokukhukuliseka kwe-acid slag kunye ne-alkaline slag. Ngenxa yokuba iqulethe i-SiO2, ukukwazi ukuxhathisa i-alkaline slag ibuthakathaka kune-acid slag. abanye. Isetyenziselwa ikakhulu uphahla lwezitovu eziqhumayo, izitovu ezitshisayo, iitophu zombane ezingaphezulu, iziko eliqhumayo, iitofu zomlilo, kunye neetofu ezijikelezayo. Ukongeza, izitena eziphezulu ze-alumina zikwasetyenziswa ngokubanzi njengezitena zokujonga iziko ezivulekileyo, iiplagi zokugalela iinkqubo, izitena zombhobho, njl.

Nangona kunjalo, ixabiso lezitena eziphezulu ze-alumina liphezulu kunezitena zodongwe, ngoko akuyimfuneko ukusebenzisa izitena eziphezulu ze-alumina apho izitena zodongwe zinokuhlangabezana neemfuno. Ixabiso lezitena eziphezulu ze-aluminium zihlala zihluka kakhulu ngokweemfuno zomxholo we-aluminium, kwaye umphumo wokusetyenziswa uhluke kakhulu.