Кампазітная цэгла з нізкай паўзучасцю для трубы з гарачым паветрам

All types of refractory materials, customized kiln plan with drawings

Product advantages: large heat storage capacity, low creep rate and other advantages.

Прымяненне прадукту: падыходзіць для падтрымкі гарачых даменных печаў і даменных печаў для сярэдніх і малых даменных печаў.

апісанне прадукту

Low-creep composite bricks for hot air ducts are made of bauxite clinker as the main raw material, supplemented by special additives, formed by high pressure, and fired at high temperature. It has the advantages of large heat storage capacity and low creep rate.

Фізіка-хімічныя паказчыкі

праект	ДРЛ-135	ДРЛ-145	ДРЛ-150	ДРЛ-165	ДРЛ-155	ДРЛ-48
Al2O3,% ≥	70	75	80	65	55	48
Refractoriness ℃ ≥	1790	1790	1790	1790	1770	1750
Apparent porosity% ≤	20	20	19	24	24	24
Compressive strength at room temperature MPa ≥	65	70	80	49	44.1	39.2
Change rate of reheating wire% ≥	± 0.1	± 0.1	± 0.1	+ 0.1 ~ -0.4	+ 0.1 ~ -0.4	+ 0.1 ~ -0.4
Change rate of reheating wire% ≥	1450℃*2h	1500℃*x2h				1450℃*2h
Load softening temperature (0.2Mpa) ℃ ≥	1500	1550	1650	1500	1470	1420
Працэнт паўзучасці% ≤	0.6 1350 × 50 гадзін	0.6	0.7	–	–	–
Працэнт паўзучасці% ≤	0.6 1350 × 50 гадзін	1450 × 50 гадзін	1500 × 50 гадзін	–	–	–