How to choose the current frequency when the induction heating furnace heats the steel pipe ?

How to choose the current frequency when the induction heating furnace heats the steel pipe ?

Induction heating furnace heating La tubería de acero es generalmente a través del calor, por lo tanto, al seleccionar la frecuencia, la corriente de estado caliente D calor debe ser mayor que el espesor de la pared de la tubería.

Table 2 – . 8 shows the solenoid induction heating steel pipe and steel optimal frequency, and Table 2.9 lists (above the Curie point) heating the steel pipe wall thickness to obtain the best highest efficiency when various frequencies.

Table 2-8 The best frequency when the spiral tube inductor heats the steel pipe and the steel pipe

Diámetro exterior del tubo / mm Wall thickness/ mm Best frequency /kHz
20 ℃ 800 ℃ 1200 ℃
Non-magnetic steel
12. 7 1 51 85 92
2 28 47 50
3 veinte uno 34 37
25.4 1 25 41 44
2 13 21 23
3 8.9 15 16
5 5.9 9. 8 11
50. The 8 1 12 20 22
2 6. 1 10. 1 11
3 4.2 6.9 7.5
5 2.6 4. 3 4.7
76.2 1 7.9 13.2 14.3
2 4 6.7 7.2
3 2.7 4.5 4.9
5 1.7 2. 8 3
102 1 5.9 9.9 10.6
2 3 5 5.4
3 2 3.4 3.6
5 1.2 2. 1 2.2
12.7 1.33 3.7 6. 3
0. 73 2 3.4
0. 54 1.5 2.5

 

Tabla 2-9 El mejor espesor de pared para el calentamiento de tuberías de acero para obtener la mayor eficiencia en varias frecuencias (cuando es más alto que el punto de Curie)

Frecuencia / Hz Diámetro / mm
5 10 20 50 100 200 300 500 10000 20000
50 25 15 7 3
150 25 10 5 2.1 1
500 20 5 2.5 1.5 0.75 0.3
1000 10 4 1.3 0.7 0.4 0. 15
2400 10 3 1.5 0.6 0. 3 0. 13
4000 5 2 0.8 0.3 0. 18 0. 07
10000 5 1.8 0.7 0. 35 0. 13 0. 08
70000 2 0.6 0.21 0. 11
440000 0.6 0.2 0. 09