Epoxy iko eriri mgbidi ọkpọkọ

Basic parameters nke epoxy iko eriri mgbidi anwụrụ:

1: Ikuku ikuku, 45 ~ 65 (enwere ike ịhazigharị akụkụ ikuku dị ka ihe dị iche iche chọrọ iji nweta ihe achọrọ ịrụ ọrụ ka mma);

2: Ọdịnaya eriri (oke ibu), 70 ~ 75%;

3: Njupụta, 2.00 g / cm3;

4: Ọnụ mmiri ntinye mmiri, ihe na-erughị 0.03%;

5: ọnụọgụ mgbasawanye nke axial, 1.8 E-05 1 / K;

6: iko mgbanwe okpomọkụ, 110～120 ℃;

7: Chemical mgbochi. Mineral mmanụ: magburu onwe ya;

8: mgbaze na itughari acid: magburu onwe ya;

9: Ụdị nkwụsị nke ngbanwe, axial 14000 MPa;

10: Ike ntakiri; axial 280 MPa; gburugburu 600 MPa;

11: ike ịkwa akwa: 150 MPa;

12: ike na-agbanwe agbanwe: 350 MPa na ntụziaka axial;

13: ike mkpakọ: axial 240 MPa;

14: ikike ikike ikwu 2-3.2;

15: Ihe nkwụsị nke Dielectric 0.003-0.015;

16: Ike mwepu akụkụ ≤5;

17: ike mkpuchi: axial 3～6 kV; radial 10 ~ 12 kV;

18: Mmetụta ọkụ: 110 KV

19: Ujo ugboro ike: 50 KV;

20: Ọkwa nguzogide ọkụ: B, F, H ọkwa

21: dayameta nke ime>5mm; dayameta mpụta <300mm; ogologo <2000mm.

环氧玻璃纤维穿墙管

环氧玻璃纤维穿墙管基本参数：

1：缠绕角，45～65（可以根据不同要求调整缠绕的角度来达到更好力学怎

2：纤维含量（重量比）, 70～75% ;

3: ọnyà, 2.00 g / cm3;

4：吸水率，小于0.03 % ;

5：轴向热膨胀系数，1.8 E-05 1/K ;

6：玻璃转化温度，110～120 ℃;

7：耐化学性能矿物油：极好；

8:溶剂及稀酸：优；

9:抗拉弹性模量，轴向 14000 MPa ；

10: 抗拉强度; 轴向 280 MPa; 环向 600 MPa;

11: 抗剪强度: 150 MPa;

12: 抗弯强度: 轴向 350 MPa;

13: 抗压强度: 轴向 240 MPa;

14：相对介电常数 2-3.2 ;

15：介质损耗因数 0.003-0.015 ;

16: 局部放电量 ≤5 ；

17: 绝缘强度: 轴向 3～6 kV;10-12 kV;

18: 雷电冲击: 110 KV

19: 工频冲击: 50 KV;

20:耐热等级: Ｂ、Ｆ、Ｈ级

21: 内径> 5mm; 外径 <300mm; 长度＜2000mm.