Pipe ea lebota la epoxy glass fiber

Pipe ea lebota la epoxy glass fiber

Mekhahlelo ea mantlha ea pipe ea lebota la epoxy glass fiber:

1: Winding angle, 45~65 (leqhubu la matsoelintsoeke le ka fetoloa ho latela litlhoko tse fapaneng ho fihlela litlhoko tse ntle tsa ts’ebetso ea mochini);

2: Likahare tsa fiber (karolelano ea boima), 70~75%;

3: Boima, 2.00 g/cm3;

4: Sekhahla sa ho monya metsi, ka tlase ho 0.03%;

5: Coefficient ea katoloso ea mocheso oa Axial, 1.8 E-05 1/K;

6: Khalase phetoho mocheso, 110~120 ℃;

7: Ho hanyetsa lik’hemik’hale. Oli ea diminerale: e ntle haholo;

8: Hlakola le ho hlapolla acid: e ntle haholo;

9: Tensile modulus ea elasticity, axial 14000 MPa;

10: Matla a thata; axial 280 MPa; circumferential 600 MPa;

11: Matla a ho kuta: 150 MPa;

12: Matla a Flexural: 350 MPa ka tataiso ea axial;

13: Matla a hatellang: axial 240 MPa;

14: Tumello e amanang le eona 2-3.2;

15: Dielectric loss factor 0.003-0.015;

16: Matla a ho ntša karolo e itseng ≤5;

17: Matla a insulation: axial 3~6 kV; mahlaseli 10~12 kV;

18: Tšusumetso ea lehalima: 110 KV

19: Tšabo ea maqhubu a matla: 50 KV;

20: Kereiti ea ho hanyetsa mocheso: B, F, H kereiti

21: bophara ba ka hare> 5mm; bophara ba ka ntle <300mm; bolelele <2000mm.

环氧玻璃纤维穿墙管

环氧玻璃纤维穿墙管基本参数:

1:缠绕角 ,45~65(可以根据不同要求调整缠绕的角度來达到更好力学性能要求);

2: 纤维含量(重量比), 70~75% ;

3:密度, 2.00 g/cm3;

4:吸水率, 小于0.03% ;

5:轴向热膨胀系数 ,1.8 E-05 1/K ;

6:玻璃转化温度 ,110~120 ℃;

7:耐化学性能 矿物油:极好;

8:溶剂及稀酸:优 ;

9:抗拉弹性模量,轴向 14000 MPa ;

10:抗拉强度;轴向 280 MPa;环向 600 MPa;

11:抗剪强度 :150 MPa ;

12:抗弯强度: 轴向 350 MPa ;

13:抗压强度:轴向 240 MPa;

14:相对介电常数 2-3.2 ;

15:介质损耗因数 0.003-0.015 ;

16:局部放电量 ≤5 ;

17:绝缘强度: 轴向 3~6 kV ;径向 10~12 kV;

18:雷电冲击: 110 KV

19:工频冲击: 50 KV ;

20: 耐热等级:B,F,H级

21: 内径 >5mm;外径 <300mm;长度<2000mm.

Pipe ea lebota la epoxy glass fiber

Mekhahlelo ea mantlha ea pipe ea lebota la epoxy glass fiber:

1: Winding angle, 45~65 (leqhubu la matsoelintsoeke le ka fetoloa ho latela litlhoko tse fapaneng ho fihlela litlhoko tse ntle tsa ts’ebetso ea mochini);

2: Likahare tsa fiber (karolelano ea boima), 70~75%;

3: Boima, 2.00 g/cm3;

4: Sekhahla sa ho monya metsi, ka tlase ho 0.03%;

5: Coefficient ea katoloso ea mocheso oa Axial, 1.8 E-05 1/K;

6: Khalase phetoho mocheso, 110~120 ℃;

7: Ho hanyetsa lik’hemik’hale. Oli ea diminerale: e ntle haholo;

8: Hlakola le ho hlapolla acid: e ntle haholo;

9: Tensile modulus ea elasticity, axial 14000 MPa;

10: Matla a thata; axial 280 MPa; circumferential 600 MPa;

11: Matla a ho kuta: 150 MPa;

12: Matla a Flexural: 350 MPa ka tataiso ea axial;

13: Matla a hatellang: axial 240 MPa;

14: Tumello e amanang le eona 2-3.2;

15: Dielectric loss factor 0.003-0.015;

16: Matla a ho ntša karolo e itseng ≤5;

17: Matla a insulation: axial 3~6 kV; mahlaseli 10~12 kV;

18: Tšusumetso ea lehalima: 110 KV

19: Tšabo ea maqhubu a matla: 50 KV;

20: Kereiti ea ho hanyetsa mocheso: B, F, H kereiti

21: bophara ba ka hare> 5mm; bophara ba ka ntle <300mm; bolelele <2000mm.