Introduction to the performance of breathable bricks

Breathable brick is a new product with long lifespan, energy saving and consumption reduction, with reasonable structural design, good thermal stability, erosion resistance, erosion resistance, and permeability resistance, high blow-through rate, safe and reliable operation, and long service life Features.

Slag resistance

재료의 슬래그 저항성 및 액체강 침투 저항성을 향상시키기 위해 일반적으로 Cr2O3 또는 크롬 커런덤의 일부가 커런덤 스피넬 통기성 벽돌에 첨가됩니다. Cr2O3와 a-Al2O3는 동일한 결정 구조를 갖는다. Cr2O3는 소재의 슬래그 저항성을 향상시킬 뿐만 아니라 소재와 용강 사이의 습윤각을 증가시켜 용강의 침투로 인한 통기성 벽돌의 기공 막힘을 크게 개선합니다.

Using Cr2O3 fine powder and Al2O3 at high temperature to form a solid solution of aluminum and chromium and an independent chromium-containing glass phase, the liquid phase formed when it comes into contact with the slag in the molten steel smelting process has a certain viscosity, thereby preventing the slag in the molten steel from affecting the air-permeable brick Corrosion; At the same time, it can absorb iron oxide and magnesium oxide in the slag, and form dense spinel in the working layer of the ventilating brick, which improves the slag resistance of the ventilating brick.

그러나 재료에 Cr2O3를 첨가한 후 고온 소성 또는 사용 후 Cr3+는 Cr6+로 산화되어 유독하고 환경을 오염시킨다. 따라서 에너지 절약 및 환경 보호를 위해 Cr2O3의 사용을 최대한 피해야 하며, 원료를 대체함으로써 Cr2O3를 첨가하지 않고 고온 성능을 Cr2O3를 첨가하는 수준에 도달할 수 있다.

내열 충격성

The main damage method of air-permeable bricks is thermal shock damage. With the continuous increase of the tapping temperature, there is a large temperature difference between working and intermittent work on the working surface of the ventilating brick, which requires the material to have extremely high thermal shock resistance. The spinel phase is introduced into the castable, and the thermal shock resistance of the air-permeable brick will be improved.

환기벽돌에 첨가된 산화물 또는 비산화물은 고온에서 골재와 고용상을 형성하여 벽돌의 고온강도를 증가시키고 벽돌의 투과성을 향상시키며 국자에 녹은 슬래그. 통기성 벽돌의 고온 열처리 후 사용 요구 사항을 충족하도록 성능이 향상됩니다.