High alumina brick implementation standard and conventional size

As a common refractory brick, high-alumina bricks have many names in daily applications. Here is a summary of the detailed popular standard names for everyone.

La composición química de la bauxita con alto contenido de alúmina En la composición química de la alúmina con alto contenido de alúmina, los componentes principales son Al2O3 y SiO2. Su composición química típica se clasifica según la composición química y el uso de la bauxita.

Los grados 1 a 6 son adecuados para minerales de tipo duraluminio monohidrato; El grado 7 es adecuado para minerales de tipo aluminio. Al2O3 es el componente principal de la bauxita. Cuanto mayor sea el contenido, mejor. La producción actual de alúmina industrial requiere que la relación de aluminio a silicio no sea inferior a 3.0. Otros óxidos se consideran impurezas. El SiO2 es una impureza nociva en la producción de alúmina por método alcalino. El alto contenido de SiO2 en la bauxita reducirá la eficiencia de producción de la fundición de corindón marrón o la producción de alúmina industrial.

TiO2 and Fe2O3 in high alumina bauxite are the two main impurities. The content of TiO2 tends to increase simultaneously with the increase of Al2O3. Studies have shown that: TiO2 in the secondary high alumina bauxite mainly forms a solid solution with mullite, and the amount of entering into the glass phase is small, which is not good for the sintering of the product, but it is beneficial to improve the high temperature mechanical properties of the product; In bauxite, TiO2 enters the glass phase more, which will increase the amount of liquid phase and reduce the viscosity of the liquid phase, which is conducive to sintering, but is not conducive to improving the high-temperature performance of the product. The alkali metal oxides K2O and Na2O of high alumina bauxite are very strong fluxes, and they produce a liquid phase at a lower temperature. When its content is too high, it will affect the phase composition and content of the clinker and the product, and adversely affect the performance of the product. The content of CaO in high alumina bauxite is generally low, about 0.2%. Its existence is detrimental to the high-temperature performance of the product, and its content is also limited in technical conditions.

1. The size of refractory brick with high alumina brick No. T-46 is a275 b230 c150 e80 d15 α 60° Volume 6565 Weight (clay brick) 13.5 Weight (semi-silica brick) 13.1 Weight (semi-silica brick) 12.5;

2. The size of refractory brick with high alumina brick No. T-47 is a275 b230 c450 e80 d15 α 60° Volume 19695 weight (clay brick) 40.4 weight (semi-silica brick) 39.4 weight (semi-silica brick) 37.5;

3. El tamaño del ladrillo refractario con alto contenido de alúmina No. T-48 es a275 b275 c150 e65 d65 α45 ° Volumen 8040 Peso (ladrillo de arcilla) 16.5 Peso (ladrillo de semisílice) 16.1 Peso (ladrillo de semisílice)

4. El tamaño de los ladrillos refractarios generales es T-3. El tamaño de los ladrillos refractarios es 230 * 113 * 65. Las dimensiones del estándar nacional y del estándar ministerial son casi del mismo largo X ancho X grosor T-1: 172 * 114 * 65, T-2: 230 * 114 * 32, T-3: 230 * 114 * 65