High alumina brick implementation standard and conventional size
High alumina brick implementation standard and conventional size
एक सामान्य रीफ्रॅक्टरी वीट म्हणून, उच्च-अल्युमिना विटा have many names in daily applications. Here is a summary of the detailed popular standard names for everyone.
उच्च अल्युमिना वीट लेबल/सामान्य नाव | आकार(मिमी) | विटांचा प्रकार |
T3 उच्च अल्युमिना वीट | * * 230 114 65 | सरळ |
T6 उच्च अल्युमिना वीट | * * 250 123 65 | सरळ |
T14 उच्च अल्युमिना वीट | * * 171 113 65 | सरळ |
T19 उच्च अल्युमिना वीट | 230 * 65 / 55 * 114 | एक्स |
T20 उच्च अल्युमिना वीट | 230 * 65 / 45 * 114 | एक्स |
T29 उच्च अल्युमिना वीट | 230 * 65 / 55 * 171 | एक्स |
T30 उच्च अल्युमिना वीट | 230 * 65 / 45 * 171 | एक्स |
T38 उच्च अल्युमिना वीट | 230 * 114 * 65 / 55 | चाकूचा प्रकार |
T39 उच्च अल्युमिना वीट | 230 * 114 * 65 / 45 | चाकूचा प्रकार |
उच्च एल्युमिना वीट दोन-तुकडा | * * 230 114 20 | सरळ |
उच्च अल्युमिना वीट तीन-तुकडा | * * 230 114 30 | सरळ |
उच्च एल्युमिना वीट क्वार्टर | * * 230 114 40 | सरळ |
उच्च एल्युमिना वीट अर्धा बार | * * 230 57 65 | सरळ |
उच्च अॅल्युमिनियम आठ विटा | * * 520 230 113 | सरळ |
दहा उच्च एल्युमिना विटांची स्थापना करा | * * 650 230 113 | सरळ |
बारा उंच अल्युमिना विटा बसवा | * * 780 230 113 | सरळ |
सपाट चार उच्च एल्युमिना विटा | * * 452 230 65 | सरळ |
G1 उच्च अल्युमिना वीट | * * 230 150 75 | सरळ |
G2 उच्च अल्युमिना वीट | * * 345 150 75 | सरळ |
G5 उच्च अल्युमिना वीट | 230 * 150 / 120 * 75 | गवताचे पाते |
G6 उच्च अल्युमिना वीट | 230 * 150 / 110 * 75 | गवताचे पाते |
The chemical composition of high alumina bauxite In the chemical composition of high alumina alumina, the main components are Al2O3 and SiO2. Its typical chemical composition is classified according to the chemical composition and use of bauxite.
ग्रेड 1 ते 6 मोनोहायड्रेट ड्युरल्युमिन प्रकारच्या धातूसाठी योग्य आहेत; ग्रेड 7 अॅल्युमिनियम प्रकारच्या धातूसाठी योग्य आहे. बॉक्साईटमधील Al2O3 हा मुख्य घटक आहे. सामग्री जितकी जास्त असेल तितके चांगले. औद्योगिक अॅल्युमिनाच्या सध्याच्या उत्पादनासाठी अॅल्युमिनियम आणि सिलिकॉनचे गुणोत्तर 3.0 पेक्षा कमी नसणे आवश्यक आहे. इतर ऑक्साईड अशुद्धता म्हणून ओळखले जातात. क्षारीय पद्धतीने अॅल्युमिनाच्या उत्पादनात SiO2 ही हानिकारक अशुद्धता आहे. बॉक्साईटमधील SiO2 ची उच्च सामग्री तपकिरी कॉरंडम वितळण्याची किंवा औद्योगिक एल्युमिना तयार करण्याची उत्पादन कार्यक्षमता कमी करेल.
TiO2 and Fe2O3 in high alumina bauxite are the two main impurities. The content of TiO2 tends to increase simultaneously with the increase of Al2O3. Studies have shown that: TiO2 in the secondary high alumina bauxite mainly forms a solid solution with mullite, and the amount of entering into the glass phase is small, which is not good for the sintering of the product, but it is beneficial to improve the high temperature mechanical properties of the product; In bauxite, TiO2 enters the glass phase more, which will increase the amount of liquid phase and reduce the viscosity of the liquid phase, which is conducive to sintering, but is not conducive to improving the high-temperature performance of the product. The alkali metal oxides K2O and Na2O of high alumina bauxite are very strong fluxes, and they produce a liquid phase at a lower temperature. When its content is too high, it will affect the phase composition and content of the clinker and the product, and adversely affect the performance of the product. The content of CaO in high alumina bauxite is generally low, about 0.2%. Its existence is detrimental to the high-temperature performance of the product, and its content is also limited in technical conditions.
1. उच्च अॅल्युमिना वीट क्रमांक T-46 सह रीफ्रॅक्टरी विटाचा आकार a275 b230 c150 e80 d15 α 60° खंड 6565 वजन (मातीची वीट) 13.5 वजन (अर्ध-सिलिका वीट) 13.1 वजन (सेमी सिलिका) 12.5 वजन;
2. उच्च अॅल्युमिना वीट क्रमांक T-47 सह रीफ्रॅक्टरी विटाचा आकार a275 b230 c450 e80 d15 α 60° खंड 19695 वजन (मातीची वीट) 40.4 वजन (अर्ध-सिलिका वीट) 39.4 वजन (अर्ध-37.5) आहे;
3. The size of refractory brick with high alumina brick No. T-48 is a275 b275 c150 e65 d65 α45° Volume 8040 Weight (clay brick) 16.5 Weight (semi-silica brick) 16.1 Weight (semi-silica brick)
4. सामान्य रीफ्रॅक्टरी विटांचा आकार T-3 आहे. रेफ्रेक्ट्री विटांचा आकार 230*113*65 आहे. राष्ट्रीय मानक आणि मंत्रालय मानक परिमाणे जवळजवळ समान लांबी X रुंदी X जाडी T-1: 172*114*65, T-2: 230*114*32, T-3: 230*114*65