Ringkasan sepuluh metode pendinginan umum dari mesin quenching frekuensi tinggi (1)

1. Single medium (water, oil, air) quenching

Single medium (water, oil, air) quenching: Quenching the workpiece that has been heated to the quenching temperature into a quenching medium to cool it completely. This is a simpler quenching method and is often used for carbon and alloy steel workpieces with simple shapes. The quenching medium is selected according to the heat transfer coefficient, hardenability, size and shape of the parts.

2. Pendinginan sedang ganda

Dual-medium quenching: The workpiece heated to the quenching temperature is first cooled to the Ms point in the quenching medium of a high-frequency heating machine with strong cooling capacity, and then transferred to the slow-cooling quenching medium to cool to room temperature to achieve different quenching cooling temperatures range, and has an ideal quenching cooling rate. It is used for complex shapes or large workpieces made of high carbon steel and alloy steel, and carbon tool steel is also mostly used in this method. Commonly used cooling media are water-oil, water-nitrate, water-air, oil-air. Generally, water is used as a quick-cooling quenching medium, oil or air is used as a slow-cooling quenching medium, and air is less used.

3. Martensite graded quenching

Pendinginan bergradasi martensit: Baja diaustenisasi, dan kemudian direndam dalam media cair (bak garam atau rendaman alkali) dengan suhu sedikit lebih tinggi atau lebih rendah dari titik Martens atas baja, disimpan untuk waktu yang tepat, dan bagian dalam dan luar bagian dari baja diperlakukan. Setelah lapisan mencapai suhu sedang, itu dibawa keluar untuk pendinginan udara, dan austenit superdingin perlahan-lahan diubah menjadi proses pendinginan martensit. Biasanya digunakan untuk benda kerja kecil dengan bentuk kompleks dan persyaratan deformasi yang ketat, dan baja kecepatan tinggi serta perkakas dan cetakan baja paduan tinggi juga biasanya dipadamkan dengan metode ini.

4. Martensite graded quenching method below Ms point

Martensitic graded quenching method below Ms point: When the bath temperature is lower than the Ms of the workpiece steel and higher than Mf, the workpiece cools faster in the bath, and the same result as the graded quenching can be obtained when the size is larger. Commonly used for larger size low hardenability steel workpieces.

5. Bainite isothermal quenching method

Bainite isothermal quenching method: The workpiece is quenched into a bath with the lower bainite temperature of the steel at an isothermal temperature, so that the lower bainite transformation occurs. Generally, it is kept in the bath for 30~60min. There are three main steps in the bainite isothermal quenching process: ① austenitizing treatment; ② cooling treatment after austenitizing;