Ringkasan sepuluh kaedah pelindapkejutan biasa bagi mesin pelindapkejutan tinggi (1)

1. Single medium (water, oil, air) quenching

Single medium (water, oil, air) quenching: Quenching the workpiece that has been heated to the quenching temperature into a quenching medium to cool it completely. This is a simpler quenching method and is often used for carbon and alloy steel workpieces with simple shapes. The quenching medium is selected according to the heat transfer coefficient, hardenability, size and shape of the parts.

2. Pelindapkejutan sederhana berganda

Dual-medium quenching: The workpiece heated to the quenching temperature is first cooled to the Ms point in the quenching medium of a high-frequency heating machine with strong cooling capacity, and then transferred to the slow-cooling quenching medium to cool to room temperature to achieve different quenching cooling temperatures range, and has an ideal quenching cooling rate. It is used for complex shapes or large workpieces made of high carbon steel and alloy steel, and carbon tool steel is also mostly used in this method. Commonly used cooling media are water-oil, water-nitrate, water-air, oil-air. Generally, water is used as a quick-cooling quenching medium, oil or air is used as a slow-cooling quenching medium, and air is less used.

3. Martensite graded quenching

Pelindapkejutan berperingkat Martensit: Keluli diaustenitkan, dan kemudian direndam dalam medium cecair (mandi garam atau mandi alkali) dengan suhu lebih tinggi sedikit atau lebih rendah daripada titik Martens atas keluli, disimpan untuk masa yang sesuai, dan bahagian dalam dan luar. bahagian keluli dirawat. Selepas lapisan mencapai suhu sederhana, ia dibawa keluar untuk penyejukan udara, dan austenit supercooled perlahan-lahan berubah menjadi proses pelindapkejutan martensit. Ia biasanya digunakan untuk bahan kerja kecil dengan bentuk kompleks dan keperluan ubah bentuk yang ketat, dan keluli berkelajuan tinggi dan alat keluli aloi tinggi dan mati juga biasanya dipadamkan dengan kaedah ini.

4. Martensite graded quenching method below Ms point

Martensitic graded quenching method below Ms point: When the bath temperature is lower than the Ms of the workpiece steel and higher than Mf, the workpiece cools faster in the bath, and the same result as the graded quenching can be obtained when the size is larger. Commonly used for larger size low hardenability steel workpieces.

5. Bainite isothermal quenching method

Bainite isothermal quenching method: The workpiece is quenched into a bath with the lower bainite temperature of the steel at an isothermal temperature, so that the lower bainite transformation occurs. Generally, it is kept in the bath for 30~60min. There are three main steps in the bainite isothermal quenching process: ① austenitizing treatment; ② cooling treatment after austenitizing;