常見的十種淬火方法總結 高頻淬火機 （1）

1. Single medium (water, oil, air) quenching

Single medium (water, oil, air) quenching: Quenching the workpiece that has been heated to the quenching temperature into a quenching medium to cool it completely. This is a simpler quenching method and is often used for carbon and alloy steel workpieces with simple shapes. The quenching medium is selected according to the heat transfer coefficient, hardenability, size and shape of the parts.

2.雙介質淬火

Dual-medium quenching: The workpiece heated to the quenching temperature is first cooled to the Ms point in the quenching medium of a high-frequency heating machine with strong cooling capacity, and then transferred to the slow-cooling quenching medium to cool to room temperature to achieve different quenching cooling temperatures range, and has an ideal quenching cooling rate. It is used for complex shapes or large workpieces made of high carbon steel and alloy steel, and carbon tool steel is also mostly used in this method. Commonly used cooling media are water-oil, water-nitrate, water-air, oil-air. Generally, water is used as a quick-cooling quenching medium, oil or air is used as a slow-cooling quenching medium, and air is less used.

3. Martensite graded quenching

馬氏體分級淬火：將鋼進行奧氏體化，然後浸入溫度略高於或低於鋼的上馬氏點的液體介質（鹽浴或鹼浴）中，保持適當的時間，內外部分鋼材經過處理。 層達到中溫後取出空冷，過冷奧氏體緩慢轉變為馬氏體淬火過程。 一般用於形狀複雜、變形要求嚴格的小型工件，高速鋼和高合金鋼工模具也常用此法淬火。

4. Martensite graded quenching method below Ms point

Martensitic graded quenching method below Ms point: When the bath temperature is lower than the Ms of the workpiece steel and higher than Mf, the workpiece cools faster in the bath, and the same result as the graded quenching can be obtained when the size is larger. Commonly used for larger size low hardenability steel workpieces.

5. Bainite isothermal quenching method

Bainite isothermal quenching method: The workpiece is quenched into a bath with the lower bainite temperature of the steel at an isothermal temperature, so that the lower bainite transformation occurs. Generally, it is kept in the bath for 30~60min. There are three main steps in the bainite isothermal quenching process: ① austenitizing treatment; ② cooling treatment after austenitizing;