Предимства на вакуумна пещ за синтероване

1. It is easier to control the carbon content: under the condition of vacuum sintering temperature, the pressure in the furnace is only tens of Pascals (Pa) or even lower, O2, N2, H2 and H2O molecules are very few, and many reactions can be ignored. The impact is very small. As long as the dewaxing process is strictly controlled, the carbon content of the alloy changes very little during the vacuum sintering process, and the performance and structure are quite stable.

2. It can improve the purity of the sintered alloy: under vacuum sintering conditions, it is beneficial to the reduction of metal oxides; the whole sintering cycle does not need to open the furnace door, no air enters, and there is almost no reaction of N2 and O2.

3. Може да подобри свойствата на твърдата фаза на сплавта: при условия на вакуумно синтероване повърхността на твърдата фаза адсорбира по-малко примеси, подобрява омокряемостта на свредлото към твърдата фаза и подобрява здравината на сплавта, особено на сплавта съдържащ TiC.

4. Процесът на работа е прост: тъй като пълнителят може да бъде пропуснат по време на вакуумно синтероване, това не само опростява операцията, но и избягва неблагоприятното въздействие на пълнителя върху повърхността на синтерованото тяло.

5. Може да се реализира различно температурно синтероване: температурата, атмосферата и налягането в пещта могат да се контролират отделно в температурни секции и може да се реализира изотермично синтероване (запазване на топлина) при всяка температура и могат да бъдат изпълнени множество функции, като например градиентно синтероване на сплав.