मोलिब्डेनम लैंथेनम मिश्र धातु गुण: मोलिब्डेनम लैंथेनम (मो-ला) मिश्र धातु और TZM मोलिब्डेनम मिश्र धातु में क्या अंतर है?

मोलिब्डेनम लैंथेनम (Mo-La) मिश्र धातु और TZM मोलिब्डेनम मिश्र धातु में क्या अंतर है?

What is a molybdenum-lanthanum alloy? Molybdenum-lanthanum alloy is an alloy composed of base metal molybdenum and lanthanum trioxide present as dispersed particles in the matrix. The content of La2O3 in the alloy is generally 0.5%~5.0% (mass fraction). To

Through the research on the high temperature performance and the corresponding structure of molybdenum-lanthanum alloy and TZM alloy at 1000~1800℃. The results show that when the temperature is lower than 1400℃, the molybdenum-lanthanum alloy has a higher comprehensive performance of strength and plasticity. When the temperature is greater than or equal to 1400℃, the tensile strength of the molybdenum-lanthanum alloy decreases, and the plasticity of the molybdenum-lanthanum alloy also decreases. With the increase of the test temperature, the tensile strength of the TZM alloy decreases, but the plasticity of the TZM molybdenum alloy increases, which is exactly the opposite of the molybdenum-lanthanum alloy.

उसी समय, चाहे वह ताकत हो या प्लास्टिसिटी, TZM मिश्र धातु की तुलना एक ही तापमान पर मोलिब्डेनम-लैंथेनम मिश्र धातु से की जाती है। माइक्रोस्ट्रक्चर अवलोकनों से पता चलता है कि ये दो मोलिब्डेनम मिश्र धातु 1100 ℃ पर पुन: क्रिस्टलीकृत होना शुरू हो जाते हैं और 1550 ℃ तक जारी रहते हैं, और उनके पुनर्नवीनीकृत अनाज लम्बी संरचना दिखाते हैं, जो शुद्ध मोलिब्डेनम की पुन: क्रिस्टलीकृत अवस्था में समान अनाज से अलग है।

1. Introduction to molybdenum lanthanum alloy

Molybdenum lanthanum alloy, also known as high temperature molybdenum, brand MoLa, is made of molybdenum doped with a small amount of lanthanum trioxide (La2O3) particles to form a so-called laminated fiber structure. This special microstructure can remain stable even at temperatures as high as 2000°C. Therefore, molybdenum-lanthanum oxide has creep resistance even under extreme conditions of use. We mainly process such molybdenum alloys into high-temperature furnace parts, such as vacuum furnace heat shields, sintering and annealing boats, stranded wires or evaporator coils.

2. मोलिब्डेनम लैंथेनम मिश्र धातु के लाभ:

उच्च पुन: क्रिस्टलीकरण तापमान;

लम्बी कण संरचना लचीलापन में सुधार कर सकती है;

मजबूत ऑक्सीकरण प्रतिरोध;

उच्च रेंगना प्रतिरोध।

3. पुन: क्रिस्टलीकरण तापमान: 1400 ℃ ~ 1500 ℃।

4. Resistivity of molybdenum-lanthanum alloy (unit: Ω*mm2/m)

तापमान ℃	20	600	1000	1200	1400	1700	1800	1900	2000
प्रतिरोधकता	0.054	0.205	0.314	0.374	0.435	0.506	0.525	0.558	0.571

5、मोलिब्डेनम लैंथेनम मिश्र धातु संरचना

ग्रेड	मुख्य संघटक%					(% से अधिक नहीं)
ग्रेड	Mo	Ti	Zr	C	La2O3	C	0	N	Fe	Ni	Si
Mo1	हाशिया	–	–	–	–	0.01	0.007	0.002	0.01	0.002	0.01
TZM	हाशिया	0.40 ~ 0.55	0.06 ~ 0.12	0.01 ~ 0.04	–	–	0.03	0.002	0.01	0.005	0.005
MoLa	हाशिया	–	–	–	0.4 ~ 1.2	0.01	–	0.002	0.01	0.002	0.01

6、Recommended surface load of molybdenum-lanthanum alloy：4~9W/cm2