Wear resistance of different composition steels after induction hardening

သံမဏိနံပါတ်	Chemical composition (mass fraction, %)			Average hardness HRC	Wear concave volume /10 3 mm 3
သံမဏိနံပါတ်	C	Mn	Cr	Average hardness HRC	Wear concave volume /10 3 mm 3
45	0.50	0.58	0 ။ 18	62	371
၁၆ မိနစ်	0.53	0 ။ 70	0 ။ 10	63	357
၄ ခ	0.42	0.55	1 ။ 10	60	329
T7	0.72	0.22	0 ။ 15	65	310

According to the data on the wear and wear resistance of induction hardened parts, the following conclusions can be drawn:

1 ) Induction heating is used to quench the surface of the workpiece, which greatly improves the wear resistance of the original unquenched workpiece.

2 ) Compared with ordinary integral hardened parts, induction hardened parts have improved wear resistance due to high surface hardness and non-decarburization.

3 ) The wear resistance of induction hardened parts made of medium carbon steel is lower than that of carburized hardened parts due to the low surface hardness and carbon content.