Bezpečnostné opatrenia pre použitie nepriepustných vetraných tehál

Out-of-furnace refining has become an important part of the modern steelmaking process. Blowing argon from the bottom of the ladle is also an important part of the refining outside the furnace. The ladle air-permeable brick is the key element to realize this process, and steel-making manufacturers are particularly concerned. A good air-permeable brick should have the characteristics of long service life, good bottom blowing effect, no (less) blowing, safe and reliable. The current breathable bricks mainly include slit type and impermeable type. The width and distribution of the slits of the slit-type ventilating bricks must be reasonably designed according to the ladle capacity, smelting steel type and the required air permeability, so the production process is more complicated; the impermeable ventilating bricks are controlled by the particle size ratio of the ingredients To produce a large number of irregularly distributed through pores, the production process is relatively simple.

Nepriepustná vzduchopriepustná tehla má štruktúru vnútorného jadra priepustného pre vzduch a husté vysokopevnostné materiály: pracovná plocha tehlového jadra je nepriepustná a bezpečnostné zariadenie má štrbinový dizajn. Pri pozorovaní štrbinového plynového kanála to indikuje priedušnosť. Ak je zvyšková výška tehly nedostatočná, je potrebné priedušnú tehlu vymeniť.

Obrázok 1 Priedušná tehla naberačky

V procese prepravy a inštalácie vzduchopriepustných tehál je potrebné zabezpečiť, aby sa nepoškodili závity koncových oceľových rúrok, aby nedošlo k uvoľneniu potrubných spojov a úniku vzduchu, čo ovplyvní prúdenie argónu a rýchlosť fúkania; zabezpečte, aby sa do koncových oceľových rúrok nedostal prach a iné nečistoty; zabezpečte, aby priedušné tehly Pracovná plocha nebola pokrytá bahnom alebo iným materiálom, aby sa predišlo neúspešnému prefúknutiu dna. Počas inštalácie alebo používania sa uistite, že potrubie je pevne pripojené a neuniká vzduch, inak je tlak argónu nedostatočný, čo ovplyvní účinok miešania a spôsobí pokles rýchlosti prefukovania.

The alloy is added too early when the converter is tapped, and the molten steel level in the ladle is too low, and the low and highly permeable alloy melting point will easily lead to poor permeability of the brick core. In addition, the premature addition of alloying leads to a lower temperature at the bottom of the ladle; if the argon blowing operation is not standardized, and the large argon gas is not stirred in time after tapping, it will easily lead to the difficulty of blowing off in the early stage of refining.

Silná inkrustácia na dne panvy, existuje veľa online naberačiek, troska môže byť vypustená včas po dokončení nalievania ocele, horúca oprava nevyfukuje priedušnú tehlu, čas zastavenia panvy je dlhý, teplota odpich roztavenej ocele je nízky atď., to všetko ľahko spôsobí povrch tehlového jadra Zvyšková roztavená oceľ a oceľová troska sa na povrchu ľahko tvoria krusty a ovplyvňujú priepustnosť vzduchu.