Naha baja 45 # kedah di-temper?
Naha baja 45 # kedah di-temper?
Kabutuhan pikeun tempering tambahan ditangtukeun ku kaayaan. Lamun tempering hawa residual bisa dikawasa salila quenching, teu perlu tambahan tempering-suhu low.
Struktur jeung sipat 45 # baja sanggeus annealing, normalizing, quenching na tempering.
45# baja annealing: ferrite + pearlite;
45 # baja normalizing: ferrite + pearlite;
45 # baja quenching: martensite;
45# baja tempering: tempered martensite (suhu low tempering), tempered troostite (suhu sedeng tempering), tempered sorbite (suhu tinggi tempering).
Struktur 45 # baja sanggeus normalizing nyaeta ferrite + struktur pearlite, struktur sanggeus quenching nyaeta struktur martensite, sarta struktur sanggeus quenching + 400 ℃ tempering nyaéta struktur troostite tempered. Teu karasa kinerja normalizing nyaeta kirang ti HB200, tapi bahan gampang machined, nu masih rencana prosés utama. Quenching +400 ℃ tempering karasa pisan alus, luhureun HB300.
Teu karasa 45 # baja quenched na tempered nyaeta antara HRC20 ~ HRC30;
The quenching karasa 45 # baja antara HRC55 ~ 58, sarta nilai bisa ngahontal HRC62;
Butuh 15-20 poé pikeun 45 # baja dipaké sabab perlu perlakuan sepuh pikeun nyaimbangkeun kinerja baja nu.
Karasa pangluhurna dina aplikasi praktis nyaéta HRC55 (frekuensi luhur quenching HRC58).
45 # baja nyaéta baja struktural karbon kualitas luhur kalawan karasa lemah sareng ngolah motong gampang. Biasana dianggo dina kapang salaku témplat, tip, tulisan pituduh, sareng sajabana, tapi peryogi perlakuan panas