Aiming na mmetụta nke dị iche iche components nke elu alumina refractory brik na arụmọrụ

Site na mmụba nke ọdịnaya Al2O3 na brik alumina refractory dị elu, ọnụ ọgụgụ nke mullite na corundum na-abawanye, na oge iko na-ebelata n’ụzọ kwekọrọ na ya, ọkụ ọkụ na njupụta nke brik alumina dị elu na-abawanye. Mgbe ọdịnaya Al2O3 dị na brik alumina dị elu na-erughị 71.8%, naanị otu kristal kwụsiri ike na-ekpo ọkụ na brik alumina refractory bụ mulllite, ọ na-abawanye na mmụba nke ọdịnaya Al2O3. Maka brik ndị na-agbanwe agbanwe yana ọdịnaya Al2O3 nke karịa 71.8%, usoro kristal kwụsiri ike na-ekpo ọkụ bụ mullite na corundum. Ka ọdịnaya nke 71.8% na-abawanye, ọnụ ọgụgụ nke corundum na-abawanye na mullite na-ebelata, na ihe ndị dị elu nke okpomọkụ. brik ndị na-agbanwe agbanwe na-emeziwanye ya.

Okpomọkụ ọkụ nke brik alumina dị elu na-adabere na sinterability nke akụrụngwa alumina. Mgbe ị na-eji ọkwa pụrụ iche na I grade bauxite clinker (nnukwu njupụta ≥ 2.80g / cm3), ihe eji eme ihe nwere nhazi edo edo na ọdịnaya adịghị ọcha dị elu, nke na-eme ka anụ ahụ na-acha akwụkwọ ndụ na-adị mfe ịmịkọrọ, mana okpomọkụ dị warara dị warara. dị mfe ịkpata oke ọkụ ma ọ bụ na-ere ọkụ. Mgbe ị na-eji Class II bauxite clinker (nnukwu njupụta ≥2.55g / cm3), n’ihi mgbasawanye na nkwụsịtụ nke kpatara mmụba nke abụọ, anụ ahụ na-acha akwụkwọ ndụ adịghị mfe ịmegharị, ya mere ọkụ ọkụ dị ntakịrị elu. Mgbe ị na-eji Class III bauxite clinker (nnukwu njupụta ≥2.45g / cm3), ihe owuwu ahụ dị oke, ọdịnaya nke Al2O3 dị ala, na ọkụ ọkụ dị ala, n’ozuzu ntakịrị elu karịa ọkụ ọkụ nke brik ụrọ clinker site na 30 ~ 50. ℃ A na-eji brik na-ekpu alumina dị elu na ọkụ na-ekpo ọkụ.