Slit-type breathable brick core

Category: Slit Breathable Brick Core

Slit-oriented air-permeable bricks Slit-oriented air-permeable bricks are commonly used structural forms of air-permeable bricks. According to the on-site use conditions, including refined steel type, refining process, ladle capacity, temperature, steel hydrostatic pressure, etc., a reasonable design of slits can make The blow-through effect of the air-permeable brick is achieved, the life span in use is increased, and the safety performance is stable. When compared with the performance of external air-permeable bricks, the air permeability and service life of the bricks are better than those of foreign advanced products, which meets the requirements of performance indicators for ladle refining production.

パフォーマンス：

1.耐スラグ性

材料の耐スラグ性と溶鋼浸透性を向上させるために、通常、Cr2O3またはクロムコランダムの一部がコランダムスピネルの通気性れんがに追加されます。 Cr2O3とa-Al2O3は同じ結晶構造を持っています。 Cr2O3は、材料の耐スラグ性を向上させるだけでなく、材料と溶鋼の間の濡れ角を増加させ、溶鋼の浸透による通気性れんがの細孔の閉塞を大幅に改善します。

Cr2O3微粉末とAl2O3を高温で使用してアルミニウム-クロム固溶体と既存のクロム含有ガラス相を形成することにより、溶鋼製錬プロセスでスラグと接触したときに形成される液相の粘度が固定されます。溶鋼中のスラグが通気性のあるレンガの腐食に影響を与えるのを防ぎます。 同時に、スラグ中の酸化鉄と酸化マグネシウムを吸収し、換気レンガの作業層に高密度スピネルを形成し、換気レンガのスラグ耐性を向上させます。

ただし、Cr2O3を材料に添加した後、高温で焼成または使用した後、Cr3 +はCr6 +に酸化され、毒性があり、環境を汚染します。 したがって、省エネや環境保護のためには、Cr2O3の使用を極力避け、原材料を入れ替えることで、Cr2O3を添加しない高温性能をCr2O3を添加するレベルに到達させることができます。

2.耐熱衝撃性

通気性れんがの主な損傷方法は、熱衝撃による損傷です。 タッピング温度が継続的に上昇するため、換気レンガの作業面での作業と断続的な作業の間に大きな温度差があり、材料は高い耐熱衝撃性を備えている必要があります。 スピネル相がキャスタブルに導入され、通気性れんがの耐熱衝撃性が向上します。

The oxide or non-oxide added in the ventilated brick forms a solid solution phase with the aggregate at high temperature, increases the high-temperature strength of the brick, improves the permeability of the brick, and resists the erosion of the ventilated brick by the molten slag in the ladle. After the high temperature heat treatment of the air-permeable brick, its performance is improved to meet its use requirements

.