Sababaraha masalah anu peryogi perhatian dina quenching frékuénsi luhur baja bearing?

1. Annealing karasa: karasa jeung struktur bagian annealed kudu inspected saméméh perlakuan panas. GCr15: 179-207HB (88-94HRB), batur 179-217HB (88-97HRB). Lamun karasa teu minuhan sarat (tinggi teuing, teuing low atawa henteu rata), alesan kudu taliti dianalisis, nu bisa mangaruhan quenching nu (kayaning teu cukup karasa, decarburization, overheating, oval badag, jsb).

2. Quenching na tempering karasa: nalika ketebalan témbok teu leuwih gede ti 12mm, sanggeus quenching, ≥63HRC, sanggeus tempering, 60-65HRC; bisa minuhan sarat karasa husus customer urang, kayaning 61-64HRC, jsb, tapi rentang kasabaran karasa sanggeus tempering Ukuran kudu kirang ti 3HRC; salila quenching normal, nilai karasa utamana gumantung kana suhu tempering.

3. Teuas uniformity: Standar stipulates yén uniformity karasa bagian sarua umumna 1HRC; lamun diaméter luar leuwih badag batan 200mm, éta 2HRC lamun teu leuwih badag batan 400mm; lamun éta leuwih badag batan 400mm, éta 3HRC.

Kinerja karasa teu cocog:

(1) karasa High: hawa quenching tinggi atawa waktu pemanasan lila, laju cooling teuing gancang, poténsi karbon tinggi (karburisasi).

(2) Teu karasa low: hawa quenching low atawa waktu pemanasan pondok, laju cooling slow, poténsi karbon low (kalawan decarburization), sarta decarburization bahan.

(3) Teu rata: hawa quenching low atawa waktu pemanasan pondok, laju cooling slow, decarburization bahan, sarta iteuk kalangkang.