High alumina brick for blast furnace

High alumina bricks for blast furnaces refer to refractory products made from high alumina bauxite clinker with an Al2O3 content of more than 48% and used to build blast furnaces. The blast furnace is the main equipment for ironmaking, and clay bricks are the lining materials that have been used very early in the blast furnace. Beginning in the 1950s, the volume of blast furnaces has grown to a large scale, and 8-12m diameter hearths have become more common. Productivity has increased rapidly. However, the furnace waist and belly corrosion obviously affect the production of Ruo blast furnace. The production process of high alumina bricks and multi-clinker clay bricks are similar. The difference is that the proportion of clinker in the ingredients is higher.

Blast furnace high alumina bricks refer to refractory products made from high alumina bauxite clinker with an Al2O3 content of more than 48% and used to build blast furnaces.

The blast furnace is the main equipment for ironmaking, and clay bricks are the lining materials that have been used very early in the blast furnace. Beginning in the 1950s, the volume of blast furnaces has grown to a large scale, and 8-12m diameter hearths have become more common. Productivity has increased rapidly. However, the furnace waist and belly corrosion obviously affect the production of Ruo blast furnace.

Craftsmanship：

The production process of high alumina bricks and multi-clinker clay bricks are similar. The difference is that the proportion of clinker in the ingredients is higher, which can be as high as 90-95%. The clinker needs to be sorted and sieved to remove iron before crushing, and the firing temperature Higher, such as Ⅰ, Ⅱ high alumina bricks are generally 1500～1600℃ when they are fired in a tunnel kiln.

Production practice in China has proved that before crushing, high-aluminum clinker is strictly sorted and classified, and stored in tiers. The use of bauxite clinker and combined clay fine grinding method can improve product quality.

fampisehoana:

a. Famerenana amin’ny laoniny

Ny tahan’ny biriky alumina avo dia avo kokoa noho ny biriky tanimanga sy biriky semi-silica, mahatratra 1750 ~ 1790 ℃, izay fitaovana marefo avo lenta.

b. Mametraha mari-pana malefaka

Satria ny vokatra avo-alumina dia manana Al2O3 avo lenta, vitsy ny fahalotoana ary vatana fitaratra tsy azo zahana, ambony kokoa noho ny biriky tanimanga ny mari-pana manalefaka entana. Na izany aza, satria ny kristaly mullite dia tsy mamorona firafitry ny tamba-jotra, ny mari-pana manalefaka entana dia mbola tsy ambony noho ny an’ny biriky silica.

d. Fanoherana fanoherana

Ny biriky alumina avo dia manana Al2O3 bebe kokoa, izay manakaiky ny fitaovana tsy miovaova tsy miandany, ary mahazaka fanoherana ny fikazan’ny solika asidra sy ny tampon’ny alkaly. Noho ny fampidirana ny SiO2, ny fahaizana manohitra ny silamo alkaly dia malemy kokoa noho ny an’ny asidra asidra.

Process points:

Natural bauxite materials require good calcination and strict classification. The iron oxide content in chemical analysis is controlled below 1.2%, and no concentrated iron spots or iron cores are allowed. High grade and high purity are required. Molded with a high-tonnage brick press, the shape of the brick is regular, and no surface net-like cracks and internal delamination are allowed. Ensure high brick density and firing temperature not lower than 1500℃.