High alumina brick for blast furnace

High alumina bricks for blast furnaces refer to refractory products made from high alumina bauxite clinker with an Al2O3 content of more than 48% and used to build blast furnaces. The blast furnace is the main equipment for ironmaking, and clay bricks are the lining materials that have been used very early in the blast furnace. Beginning in the 1950s, the volume of blast furnaces has grown to a large scale, and 8-12m diameter hearths have become more common. Productivity has increased rapidly. However, the furnace waist and belly corrosion obviously affect the production of Ruo blast furnace. The production process of high alumina bricks and multi-clinker clay bricks are similar. The difference is that the proportion of clinker in the ingredients is higher.

Blast furnace high alumina bricks refer to refractory products made from high alumina bauxite clinker with an Al2O3 content of more than 48% and used to build blast furnaces.

The blast furnace is the main equipment for ironmaking, and clay bricks are the lining materials that have been used very early in the blast furnace. Beginning in the 1950s, the volume of blast furnaces has grown to a large scale, and 8-12m diameter hearths have become more common. Productivity has increased rapidly. However, the furnace waist and belly corrosion obviously affect the production of Ruo blast furnace.

Craftsmanship：

The production process of high alumina bricks and multi-clinker clay bricks are similar. The difference is that the proportion of clinker in the ingredients is higher, which can be as high as 90-95%. The clinker needs to be sorted and sieved to remove iron before crushing, and the firing temperature Higher, such as Ⅰ, Ⅱ high alumina bricks are generally 1500～1600℃ when they are fired in a tunnel kiln.

Production practice in China has proved that before crushing, high-aluminum clinker is strictly sorted and classified, and stored in tiers. The use of bauxite clinker and combined clay fine grinding method can improve product quality.

性能：

一種。 耐火度

高鋁磚的耐火度高於粘土磚和半矽磚，達到1750~1790℃，是一種優質的耐火材料。

灣荷重軟化溫度

由於高鋁製品Al2O3高，雜質少，易熔玻璃體少，荷重軟化溫度比粘土磚高。 但由於莫來石晶體不形成網狀結構，荷重軟化溫度仍不如矽磚高。

C。 抗渣性

高鋁磚含有較多的Al2O3，接近中性耐火材料，能抵抗酸性渣和鹼性渣的侵蝕。 由於含有SiO2，抗鹼性渣的能力弱於酸性渣。

Process points:

Natural bauxite materials require good calcination and strict classification. The iron oxide content in chemical analysis is controlled below 1.2%, and no concentrated iron spots or iron cores are allowed. High grade and high purity are required. Molded with a high-tonnage brick press, the shape of the brick is regular, and no surface net-like cracks and internal delamination are allowed. Ensure high brick density and firing temperature not lower than 1500℃.