Introduction to the lamination of self-lubricating board mica board

Introduction to the lamination of self-lubricating board mica board

1. Tape cutting: The process is to cut the tape to a certain size. The cutting equipment can be a continuous fixed-length slicer, or it can be cut by hand. For tape cutting, the size is required to be accurate. Stack the cut tapes neatly, stack the tapes with different glue content and fluidity separately, and record and store them for later use.

2. Adhesive cloth selection: The process of adhesive cloth selection is very important to the quality of the laminate. If the selection is improper, the laminate will be cracked and the surface spattered and other defects will occur. On the surface layer of the selected board, 2 sheets of adhesive tape with high surface glue content and high fluidity should be placed on each side. The volatile content should not be too large. If the volatile content is too large, it should be dried before use.

3. Hot pressing process: The most critical process in the pressing process is process parameters, among which the most important process parameters are temperature, pressure and time. Overcome the vapour pressure of volatiles, make the bonded resin flow, and make the adhesive layer closely contact; prevent the plate from being deformed when it is cooled. The size of the molding pressure is determined according to the curing characteristics of the resin. Usually the epoxy/phenolic laminate is 5.9MPa, and the epoxy sheet is 3.9-5.9MPa.

4. Post-treatment: The purpose of post-treatment is to further cure the resin until it is completely cured, while partially eliminating the internal stress of the product and improving the bonding performance of the product. The post-treatment of epoxy board and epoxy/phenolic board is kept at a temperature of 130-150℃ for about 150min.