वृत्ताकार आरी के विरूपण को रोकने के उपाय high-frequency hardening machine quenching and leveling methods

1. The saw board should enter the cooling medium vertically during quenching, so that both ends of the saw board are cooled at the same time. When oil is used as the quenching cooling medium, it is generally better to control it at 60-90°C. If the oil temperature is lower than 50℃, the deformation of the saw board will increase, and there is a potential risk of quenching cracking. In order to reduce stress, austempering or graded quenching can be used.

2. सख्त सुनिश्चित करने के आधार के तहत, वर्कपीस पर विद्युत चुम्बकीय तरंगों के प्रभाव को कम करने के लिए पावर-ऑफ हीटिंग की विधि अपनाई जाती है।

3. When the leveling still fails to meet the requirements after two phase changes, you can use a cold hammer for leveling, but the hammering technology is very demanding, and the deformation will increase if it is not correct.

4. The Ms point of 65Mn steel is about 270℃. When the martensitic transformation occurs, the plasticity of the steel is very good. If the saw board is placed between the two plates at this time, it can be forced to level.

5. चरण परिवर्तन प्रक्रिया जो तब होती है जब आरा बोर्ड को तड़का दिया जाता है, का उपयोग आगे के स्तर के लिए किया जा सकता है। स्टैकिंग के दौरान संचित त्रुटि को कम करने के लिए तड़के से पहले आरा ब्लेड की सतह को साफ करें। तड़के को एक सपाट प्लेट से दबाया जाना चाहिए और तड़के का समय पर्याप्त होना चाहिए।

6. हीटिंग तापमान को ऊपरी सीमा लेनी चाहिए, और देखा बोर्ड की आंतरिक संरचना को स्थिर करने के लिए हीटिंग का समय पर्याप्त होना चाहिए, एमएस बिंदु को कम करना, शमन के बाद बनाए रखा ऑस्टेनाइट की मात्रा में वृद्धि करना, और देखा बोर्ड के विरूपण को कम करना .