Gqoka ukumelana kwe-carburizing kanye ne-induction hard specimens
Gqoka ukumelana kwe-carburizing kanye ne-induction hard specimens
| Ibanga lensimbi | Inqubo yokwelashwa kokushisa | ubulukhuni
HV |
Gqoka / mg | |
| Sample | Ukuthwala ithusi | |||
| 18Cr2Ni4WA | ICarburizing 1.5mm, 780%: ukucisha, ukufuthelana ngo-170 ℃ | 675 | 0.5 | 4.5 |
| 40CrNiMoA | Ukucisha i-860T, i-550V tempering, induction quenching 1mm deep,
Ukushisa ku-18O ℃ |
748 | 4.5 | 4.0 |
| 10 | I-Carburizing 1.5mm, icisha ku-780 ℃, i-tempering ngo-170 ℃ | 782 | 1.0 | 3.0 |
| 45 | Ukucisha i-860Y, i-550 ℃ tempering
Lokungeniswa lukhuni u-1mm ukujula, kuthobekile ku-180 ℃ |
748 | 7.0 | 3. 8 |
Ukumelana okuphezulu kokugqoka kwensimbi e-carburized kungenxa yokuqukethwe kwekhabhoni ephezulu kungqimba olungaphezulu. Lapho i-carbon steel w (C) ingaphansi kuka-0.43%, ingxenye e-carburized inenzuzo ekumelaneni kokugqoka, futhi lapho w (C) Uma ingaphezulu kuka-0.45%, ukumelana nokugqoka kwezingxenye eziqinisiwe zokungeniswa kuyathuthukiswa. Lesi yisiphetho sokuthi i-TH HACAHOBA idonse ngokuya ngokuhlolwa kwenkambu kwephini lethrekhi. Ngakho-ke, iphini yethrekhi yogandaganda ithathelwa indawo yinqubo entsha yokuqinisa insimbi yensimbi engama-50. . Ukuqhathaniswa kokumelana nokugqoka kwama-w (C) wensimbi ahlukile ngemuva kokucinywa kokungeniswa kukhombisa ithonya lokwakheka kwensimbi. Imininingwane esetafuleni ifakazela ukuthi insimbi ye-T7 inenani elincane kakhulu lokugqoka, futhi okuqukethwe yikhabhoni nobulukhuni nakho kuphezulu kakhulu; Insimbi engu-45 kanye no-50Mn inokuqina kokugqoka okufanayo; Insimbi engu-45Cr inokumelana nokuguga phakathi kwensimbi ye-T7 nensimbi engu-50Mn, okukhombisa ukuthi insimbi eku-Conting Ming ingathuthukisa ukumelana nomhuzuko.