Brændingsprocessen af ​​lersten produceret af ildfast mursten fabrikanter

Indløbstemperatur for tørremedium: 150~200C (standard mursten og almindelig mursten)

120 ~ 160 ℃ (Specialformet mursten)

Udstødningstemperatur: 70 ~ 80 ℃

The residual moisture of the brick is less than 2%

Tørretid: 16~24 timer

Brændingen af ​​lersten kan opdeles i fire faser

1. Normal temperatur til 200 grader Celsius: På dette tidspunkt bør temperaturen ikke være for hurtig for at forhindre kroppen i at revne. Ved fyring i en tunnelovn bør temperaturen på de første 4 parkeringspladser ikke overstige 200 ℃

2, 200~900C: På dette stadium bør opvarmningshastigheden øges for at lette den kemiske reaktion af organisk materiale og urenheder i greenen.

Within the temperature range of 600～900℃, a strong oxidizing atmosphere should be maintained in the kiln to prevent the occurrence of “black core” waste

3 ℃ til den højeste brændingstemperatur: I højtemperaturstadiet skal temperaturen stige støt og fortsætte med at opretholde en oxiderende atmosfære, så den defekte krop opvarmes jævnt, og samtidig kan den også forhindre mursten fra revner. Fordi sintringskrympningen er meget stærk over 900c, er krympningshastigheden så høj som 1100%, så det er meget vigtigt at opretholde afslapningen af ​​temperaturgradienten og eliminere den indre spænding.

The fire resistance temperature of clay bricks is generally 100-150C higher than the sintering temperature. If the sintering temperature range of the sintered clay is narrow, the refractory temperature should be lower, preferably around 50-100C. The sintering temperature of clay bricks should ensure that the combined clay is fully softened, and the surface layer of the fine powder and coarse particles of the clinker is fully reacted, so that the clinker particles can be bonded, so that the product can obtain proper strength and volume stability. The sintering temperature is generally 1250～1350c. When the content of al2o3 is high, the sintering temperature of the product should be appropriately increased, about 1350～1380c, and the heating time is generally 2-10h to ensure sufficient reaction in the product and consistent product quality.

4 Afkølingstrin: Ifølge gitterændringen af ​​lerstenen i kølesektionen skal kølehastigheden reduceres hurtigt, når temperaturen er over 800 ~ 1000 ℃, og kølehastigheden skal sænkes til under 800 ℃. Faktisk vil den faktiske anvendte afkølingshastighed i den faktiske produktion ikke forårsage risikoen for koldrevner af produktet.