丸鋼焼入れ焼戻し炉
丸鋼焼入れ焼戻し炉
The round steel quenching and tempering furnace mainly uses induction heating modulated by round steel, bar stock, wire, and steel rod to realize the quenching and tempering function.
1. Main technical indicators of round steel quenching and tempering furnace production line
1. Quenched and tempered material: 30MnSi
2.丸鋼およびワイヤーの仕様：Φ7.1-Φ12.6mm
3.焼入れ温度：930-960℃焼戻し温度：400-460℃
4.丸鋼焼入れ焼戻し炉の加熱消費電力：約370度/トン
5.丸鋼焼入れ焼戻し炉の作業モード：連続作業システム
6.丸鋼焼入れ焼戻し炉生産ラインの中心高さ：1000mm
7. Feeding direction of round steel quenching and tempering furnace production line: left (right) feed
8.丸鋼焼入れ焼戻し炉の配電要件：各ラインの総設備容量：1250KVA年
9. Round steel quenching and tempering furnace output: 60,000 tons/year, consisting of 4 lines.
10.丸鋼焼入れ焼戻し炉生産ラインの最高運転ライン速度：
Φ7.1mm———— 100m / min
Φ9.0mm———— 90m / min
Φ10.7mm———– 60m / min
Φ12.6mm———– 40m / min
12. Cooling water requirements for round steel quenching and tempering furnace production line (single line):
NS。 製品循環冷却水
流量：100m3 / h圧力：0.4MPa
Water temperature: not higher than 33℃
Water quality: Urban water supply water quality standard CJ/T206-2005 (Ministry of Construction)
NS。 誘導加熱炉の冷却水：
流量：100m3 / h圧力：0.4MPa
Water temperature: not higher than 33℃
Water quality: Urban water supply water quality standard CJ/T206-2005 (Ministry of Construction)
c. Compressed air requirements (single line):
投与量：3m3 / min圧力：0.6MPa水温：33℃以下
Compressed air quality: GB/T13277-91 “Compressed air quality grade for general use”
2.丸鋼焼入れ焼戻し炉の生産ラインの設備構成と説明：
各丸鋼焼入れ焼戻し炉PC棒鋼は、ドローイング成形装置、牽引伝達装置、全固体静的周波数変換加熱電源、誘導加熱炉、スプレー冷却水タンク、油圧せん断および反転装置、ワイヤー巻き取りによって製造されます。機器、ACモーター可変周波数制御システム、PLC制御システム、温度測定システム、中央集中制御ユニットで構成されています。
各生産ライン機器には、具体的に次のものが含まれます。
1. Mechanical part:
ペイオフラックセット
ケーブル管理フレーム1
機械的防錆機1
Drawing forming machine 1
矯正機1セット
洗浄機1
1#Towing machine 1 set
Quenching water tank 1
テンパリングシンク1
2＃トラクションマシン1セット
油圧せん断反転機1セット
Take-up machine 2
2.丸鋼焼入れ焼戻し炉の構成：
KGPS-500KW/6KHZ medium frequency induction heating power supply 1 set
CYP-200KW / 40KHZIGBT超低周波誘導加熱電源1セット
CYP-200KW / 50HZIGBT超低周波誘導加熱電源1セット
KGPS-250KW/8KHZ KGPS intermediate frequency induction heating power supply 1 set
周波数変換キャビネットXNUMXセット
90KW（伸線機ドライブ）1セット
5.5KW（スコアリングマシンのドライブ）1セット
11KW（トラクター駆動）2セット
4KW（巻き取り機の駆動）2セット
Operation console and operation box 6 sets
メインコンソール1
巻き取り操作ボックス2セット
ジョグ操作ボックス（機械式スケール除去、トラクター、製図機各）3セット
温度計（温度測定範囲300-1000℃）XNUMX
3. Mechanical equipment composition and technical performance of round steel quenching and tempering furnace
（1）ペイオフフレームのダブルアーム回転構造、センタースリーブはベアリングを介して固定支柱に接続され、センタースリーブは軽く回転および配置でき、線材サスペンションアームはセンターに接続されますスリーブはボルトで交換でき、リール交換時に軽く回転し、ペイオフ時に配置できます。線材の頭と尾をつなぐと便利です。
（2）ワイヤー管理フレームワイヤー管理フレームはテーパー構造であり、ワイヤーの乱れを防ぐためにワイヤーロッドリングの形状を直線状に変更することを目的としています。
(3) Mechanical rust remover The mechanical rust remover consists of 2 sets of 90-degree repeated bending rollers. Driven by motor-lifter-lead screw (or pneumatic), the movable bending roller is pushed to extend or retract. Ensure sufficient bending angle between the steel bar and the bending roller to peel off the oxide scale to the maximum. After the oxide skin is peeled off, it falls into the collection tank below for easy cleaning. Fully sealed structure is adopted to prevent dust from escaping in the workshop.
(4) The PC steel rod concave thread forming of the drawing machine adopts the method of matching the drawing speed and the rotation speed of the mold. The mold is well stressed, the mold life is long, and the lead of the steel rod is artificially controlled to ensure the appearance quality of the product. The reducer of the wire drawing machine adopts a medium-hard tooth surface reducer, and there are protective devices at the tank body and the belt. The wire drawing tank is equipped with a shut-down pneumatic pinch roller to prevent the machine from shutting down and disordering the line. The diameter of the reel is 900mm, the maximum drawing speed is 100m/min, the wire drawing machine motor is 90KW, and the rotary die motor is 5.5KW.
（5）矯正機矯正機はパッシブで、互いに90度を形成するXNUMX組の曲げロールで構成されています。 トラクターの力で、それは鋼棒をまっすぐにし、まっすぐにする張力を形成します。
（6）洗濯機洗濯機は、モーターで駆動する2組の鋼線ホイールで構成され、鋼棒の表面の破片を除去します。 モーターは0.55KWで、レデューサーは無段変速機レデューサーです。
(7) There are two tractors. They are respectively placed in front of the quenching heating furnace, and after the tempering and cooling device, they play the role of full-line dragging. The traction machine is composed of three pairs of traction rollers, the lower roller is active and the upper roller is passive. The lower roller device is on the output of a non-standard transmission box with a single shaft input and three output shafts. The upper roller device is in the chute of the upper sliding frame. Keep to ensure the clamping force of the steel bar and ensure the smooth operation of the steel bar. The two tractors adopt micro-tension control technology, which can adjust the tension at any time according to the process needs and keep it between the two tractors. The micro-tension control technology can be used to adjust the tension and maintain at any time according to the process needs, which is automatic control between the two tractors. Under the formation of constant tension to provide guarantee to meet the needs of product quality. The traction roller is composed of two grooves, and the traction roller is arranged on the optical axis through an expansion sleeve to facilitate the replacement of the traction roller. The motor is 11KW, and the reducer is a planetary cycloid reducer.
（8）焼入れ焼戻し冷却装置焼入れ焼戻し冷却装置はステンレス鋼板製で、冷却方法は水冷、出口端には送風装置を備えています。 焼入れタンクの長さは6メートル、焼き戻しタンクの長さは5メートルです。
（9）油圧反転せん断機は、生産ラインの迅速な切断の要件に応じた同期切断と反転を保証し、100％のせん断反転を保証し、生産ラインの継続的な運用を保証します。 油圧ステーションのモーターは2.2KWです。
（10）巻き取り機は棒鋼ペイオフの要件に合わせて設計されており、巻き取りリールの回転速度は棒鋼の回転速度に応じて定期的に変化し、規則的な配線を実現します。 モーターは4kwで、減速機はウォームギア減速機です。 