Boea ba maqhubu a mahareng bo pheha setene se phefumolohang
Boea ba maqhubu a mahareng bo pheha setene se phefumolohang
Lebitso la sehlahisoa:
Setene se phefumolohang bakeng sa ho butsoela tlase seboping sa maqhubu a mahareng
Sehlopha: Litene tse ka Phefumolohang tsa ho Foka ka Tlase ho Sebōpi sa Maqhubu a Mahareng
Details Product
Ts’ebetso e phahameng ea mocheso oa litene tse kenang kahare bakeng sa sebōpi se mahareng se its’etleha haholo ka sebopeho sa ‘mele, lik’hemik’hale le liminerale tsa thepa e sebelisitsoeng e sa sebetseng. Tongyao ke mofani oa thepa e qhekellang indastering, ‘me tlhahiso ea litene tse kenang moeeng bakeng sa ho butsoa ka tlase ho sebopi sa maqhubu a mahareng e sebelisitsoe haholo. kopo.
Ts’ebeliso ea Breathable Brick Refining Technology ho Medium Frequency Induction Furnace
Ka ts’ebeliso ea litene tse kenang moeeng, re khutsufalitse mahlale a mahlale a ho hloekisa a maqhubu a mahareng, a fetotseng sebopi se tloaelehileng sa maqhubu a maqhubu ho tloha “tšepe ea lik’hemik’hale” ho ea ho a tšepe. Maemong a mangata, boleng ba tšepe e qhibilihisitsoeng (taijin) bo fihlile seboping sa AOD le seboneng sa LF se hloekisang. , Boemo ba boleng ba VD vacuum degassing sebopi bo hloekisang.
Khase e hlokahalang (joalo ka argon e hloekileng) e romelloa tšepe e qhibilihisitsoeng ka setene se kenang moeeng, mme kamora palo e itseng le nako ea phallo, li ka kenyelletsoa (joalo ka Sio2, Al2O3, MgO, jj.) fokotsehile. ‘Me 【O】 【N】 【H】 dikahare, ho na le litlhokahalo tse ikhethang joalo ka ha u fokotsa matla, o ka letsa khase e tsoakiloeng ea argon / oksijene, e ka fokotsang khabone kahare ho mofuta o itseng, ha o kopana le tšepe ea naetrojene, e butsoang ka nitrojene e ka ba Eketsa ammonia.
MOLAO OA HO SEBETSA Ts’ebetso ea ho hloekisa ka ho tšela khase ea argon ka seboping sa induction ke kamora hore tšepe e qhibilihisitsoeng e qhibilihe. Kamora hore deoxygenation ea pele e phetheloe, kamora ho etsa sampole le ho e hlahloba, khase ea argon e nang le bohloeki bo phahameng e hlahisoa ka tšepe e qhibilihisitsoeng ka setene se kenang kahare sa sebopi. Ha khase ea argon e feta ka setene se kenang moeeng, e na le boemo bo phahameng ba ho hasana, e theha karoloana e nyane ka lebelo le leholo le nyolohang. Phallo ea bubble, li-bubble tse ngata tse fetang ka tšepe e qhibilihisitsoeng li tla hlahisa phello ea ho hloekisa. Phofo e ‘ngoe le e’ ngoe ea argon kahare ho tšepe e qhibilihisitsoeng ke “kamore ea lephaka” e nyane, ‘me H, O, N le likhase tse ling ha li eo kahara bubble ea argon. Ka mantsoe a mang, khatello e fokolang ea likhase tsena ka bubble ea argon e lekana le zero. Ha bubble ea argon e nang le khatello e phahameng e sa feteng ka tšepe e qhibilihisitsoeng, [H] [O] [N] e qhibilihisitsoeng le c0 e sa qhalloang e tla kenella ka har’a bubble ea argon ebe e latela bubble Rise and overflow. E le ho fihlela sepheo sa ho fokotsa.
Kamora ho hloekisa, boleng le ho hloeka ha tšepe li ntlafalitsoe haholo, phapang ea li-inclusions pele le kamora ho hloekisoa e fokotsehile haholo, mme khase e fokotsehile haholo. Mohlala hona joale o bapisoa le o latelang
1. Kenyelletso: Mokhoa oa tlhahlobo ea microscopic bakeng sa lits’oants’o tse sa tšepe ka tšepe ea GB10561-2005
Ntho ea ABCD
Sulfide ea alumina silicate Ball oxide e
Karolelano pele e hloekisoa 1.8 1.7 1.5 2.1
Karolelano ka mor’a ho hloekisa 0.55 0.64 0.5 0.67
Phokotso ea karolelano% 69 62 67 68
projeke | A | B | C | D |
Sebabole | Alumina | Tiile | Ball oxide | |
Karolelano pele e hloekisoa | 1.8 | 1.7 | 1.5 | 2.1 |
Karolelano ka mor’a ho hloekisoa | 0.55 | 0.64 | 0.5 | 0.67 |
Karolelano ea phokotso ea% | 69 | 62 | 67 | 68 |
Liphetho tsa nnete tsa litekanyo li fihlela litlhoko tsa tekheniki ea maemo.
2. Boitsebiso ba haedrojene bo ka tlase ho 1.0ppm, bo fihlella litlhokahalo tsa die steel ≤2.5ppm, le limaraka tse ling tsa tšepe ≤3.0ppm.
3. Lintho tse nang le oksijene li ka tlase ho 0.0050%.
4. Ka mor’a hore ingot ea tšepe e sebetsane, tlhahlobo ea mahlaseli e fihlile boemong ba bobeli ba (GB / T13315-1991).
5. Ho bapisa thepa ea mochini oa tšepe e sa hloekang e 304 le ntle le ho hloekisoa: (GB / T328-2002)
1) Matla a tensile ke 549.53Mpa pele e hloekisoa le 606.82Mpa kamora ho hloekisoa e eketsoa ka 57.29Mpa
2) Matla a kotulo ke 270Mpa pele e hloekisoa le 339.52Mpa kamora ho hloekisoa e eketsoa ka 69.52Mpa
3) Force 38.46KN pele u hloekisa 49.10KN kamora ho hloekisa Keketseho ka 10.64KN
Lintlha tse ‘maloa:
a) Kaha nako ea ho thunya ea argon bakeng sa sebopi ka seng sa tšepe ke 5 ~ 10mm, ho letsa argon ho etsoa kamora ho eketsa Taijin. Kamora ho foka, ho tlanya tšepe ho ke ke ha ama nako ea ho qhibilihisa ebile ho ke ke ha eketsa ts’ebeliso ea matla.
b) Ho tlosoa ha [N] [H] [O] ka ho letsa khase ea argon ha ho bake tšisinyeho ea lik’hemik’hale, eseng feela ho ke ke ha khutsufatsa bophelo ba lera la sebopi, empa ho fapana le hoo, bophelo ba lera la sebopi bo lelele ho homogenization ea mocheso o qhibilihang sebōping.
c) Argon ke khase ea maikutlo mme e bolokehile haholo ho e sebelisa.
Ka bokhutšoanyane: Theknoloji ea ho hloekisa sebōpi sa maqhubu a mahareng e tšoauoang ke ts’ebeliso ea litene tse kenang moeeng ke ts’ebetso ea tlhahiso e nang le matsete a tlase, phihlello e potlakileng, theko e tlase le boleng bo holimo. Ke ts’ebetso ea tlhahiso e bolokang matla le e bolokang tikoloho ebile ke ts’ebetso ea tlhahiso ea phallo e khuts’oane. Ho ipapisitsoe le theknoloji ena, e kopantsoeng le ts’ebetso e sireletsang ea ho betsa, lihlahisoa tsa boleng bo holimo le lihlahisoa tsa tšepe li ka hlahisoa.