300kg tanpon vag aliminyòm fonn gwo founo dife
300kg tanpon vag aliminyòm fonn gwo founo dife
Buffer wave aluminum melting furnace is a kind of metal melting equipment developed by our company that is suitable for below 950℃. Its functions have the following characteristics:
1. Ekonomize enèji ak ekonomize lajan: konsomasyon elektrisite an mwayèn nan aliminyòm se 0.4-0.5 kWh / KG aliminyòm, ki se plis pase 30% mwens pase recho tradisyonèl yo;
2. Itilizasyon efikas: 600 ° tanperati k ap monte nan 1 èdtan, vitès chofaj super vit, ki dire lontan tanperati konstan;
3. Pwoteksyon anviwònman ak kabòn ki ba: nan liy ak ekonomi enèji nasyonal ak politik rediksyon emisyon, pa gen pousyè, pa gen okenn lafimen lwil oliv, e pa gen okenn emisyon gaz danjere;
4. Sekirite ak estabilite: rechèch endepandan ak devlopman nan teknoloji 32-bit CPU, ak pwoteksyon entelijan tankou flit, flit aliminyòm, debòde, ak echèk pouvwa;
5. Mwens salop aliminyòm: tanpon vag eddy aktyèl chofaj endiksyon, pa gen okenn ang mouri chofaj, segondè pousantaj itilizasyon materyèl bwit;
6. Ekstansyon lavi: creuset la chofe respire, diferans tanperati a piti, epi esperans lavi a pwolonje pa 50% an mwayèn;
7. Temperature control: the eddy current reacts instantly, the crucible heats up by itself, without the hysteresis of traditional heating;
1. Endistri aplikab:
Aliminyòm mouri-Distribisyon plant, aliminyòm ingot pwodiksyon plant, dechè aliminyòm endistri k ap fonn, Distribisyon plant, otomobil ak motosiklèt Pwodwi pou Telefòn pwodiksyon, koki telefòn mobil, lanp, elektrik diri cuisinier chofaj plak manifakti
2. Pwodwi entwodiksyon:
Buffer wave aluminum melting furnace is an energy-saving buffer wave aluminum melting equipment that replaces traditional resistance, coal-fired, oil-fired, and intermediate frequency furnaces. With the increase in cost of materials, various industries are facing fierce market competition. The metallurgical industry has worsened the situation. The emergence of the buffer wave aluminum melting furnace has solved various problems in the metallurgical industry. It has the advantages of intelligence, safety, money saving, environmental protection and other national support, and is sought after by the metallurgical industry.
3. 300 kg buffer wave aluminum melting furnace
Modèl: SD-AI-300KG
K ap fonn materyèl: Silisyòm carbure grafit kriz
Kreze materyèl: alyaj aliminyòm
Kreze kapasite: 300KG
Rated pouvwa: 60KW
Melting power consumption/ton: 380 kWh/ton
Konsèvasyon pouvwa chalè konsomasyon / èdtan: 3 kWh / èdtan
Vitès k ap fonn kg / èdtan: 160KG / èdtan
Buffer wave aluminum melting furnace product specification selection:
Nimewo pwodwi | pouvwa | kapasite | Rated Kapasite | Opere tanperati | Vide tan chofaj gwo founo dife | 坩埚 type |
SD-RL-100 | 30KW | 100KG | 40KG / H | 950 degre | <1.5H | Fòm wonn |
SD-RL-200 | 40KW | 200KG | 100KG / H | <1.5H | ||
SD-RL-300 | 60KW | 300KG | 180KG / H | <2.0H | ||
SD-RL-400 | 80KW | 400KG | 240KG / H | <2.0H | ||
SD-RL-500 | 100KW | 500KG | 300KG / H | <2.5H | ||
SD-RL-600 | 120KW | 600KG | 350KG / H | <2.5H | ||
SD-RL-800 | 150KW | 800KG | 420KG / H | <2.5H | ||
Remarks: Various furnaces can be customized according to different occasions and technical requirements of customers. |
4. prensip chofaj:
The buffer wave aluminum melting furnace uses a buffer wave induction heating controller to convert electrical energy into heat energy using the principle of buffer wave induction heating. First, the internal rectifier filter circuit converts the alternating current into direct current, and then the control circuit converts the direct current into high-frequency magnetic energy. The high-speed changing current passing through the coil will produce a high-speed changing magnetic field. When the magnetic field lines in the magnetic field pass through the crucible, numerous small eddy currents will be generated inside the crucible, so that the crucible itself will generate heat at high speed, transfer the heat to the aluminum alloy, and melt into a liquid state. .
Measures to reduce aluminum slag in buffer wave aluminum melting furnace:
In the process of aluminum alloy smelting, as the amount of slag increases, the melting loss of aluminum also increases, and the amount of slag is related to the melting temperature, the state of the charge, and the production process. If you want to reduce aluminum slag, you must start from the following aspects:
(1) Reasonable furnace geometric dimensions and feeding order;
(2) Strictly control the melting temperature to prevent overheating. The flame spray should have a certain angle to facilitate rapid melting and shorten the melting time;
(3) Suitable melting amount and refining time, stirring should be stable, without destroying the oxide film on the surface of the melt, and covering the aluminum melt in a timely manner;
(4) Sort and clean the waste aluminum, and pack the finely divided charge with a large contrast surface area with a press;
(5) Treatment of slag before slagging;