Defects of traditional steel rolling process

Jounal traditional steel rolling process is that the steel billets are stacked and cooled, transported to the rolling mill, and then heated in a heating furnace to be rolled into steel. This process has two defects:

1. Apre yo fin tire billet la soti nan kaster kontinyèl ki fè asye, tanperati a sou kabann nan refwadisman se 700-900 ° C, ak chalè inaktif nan billet la pa efektivman itilize.

2. After the continuous casting billet is heated by the heating furnace, the surface of the billet will lose about 1.5% due to oxidation.

Analiz benefis ekonomize enèji:

1. Konsomasyon chabon nan pwosesis orijinal la chofaj gwo founo chofaj se 80 kg / tòn asye (valè kalorifik 6400 kcal / kg), ki ekivalan a 72 kg nan chabon estanda; apre transfòmasyon teknolojik la, konsomasyon enèji pwosesis la se 38 kWh pou chak tòn asye, ki ekivalan a 13.3 kg chabon estanda.

2. Ki baze sou pwodiksyon anyèl estime pwodwi asye nan 600,000 tòn, ekonomi anyèl estanda chabon se: (72-13.3) ÷ 1000 × 600,000 tòn = 35,220 tòn estanda chabon.

3. Prensip ekonomize enèji:

Apre billet la trase soti nan machin nan Distribisyon kontinyèl, sifas la gen yon tanperati 750-850, ak tanperati a entèn se menm kòm yon wo 950-1000 ° C. Youn nan prensip debaz yo nan chofaj endiksyon se efè a po, ki se ke enèji chalè se piti piti transfere andedan soti nan chofaj la sifas. Pi wo pase, yon tyè nan andedan billet la pa bezwen chofe. Dapre diferan dimansyon kwa-seksyonèl billet, chwazi diferan frekans pou jwenn pi bon efikasite chofaj.

4. Pwen ekonomize enèji:

a) Pousantaj nan itilizasyon enèji segondè nan chofaj endiksyon ka kòm yon wo 65 a 75%, pandan y ap tradisyonèl founo chofaj rejeneratif la se sèlman 25 a 30%.

b) Oksidasyon sifas nan billet chofaj endiksyon an se sèlman 0.5%, pandan y ap founo rejeneratif la ka rive jwenn 1.5-2%.